Gray,

I did get a Tungsten Carbide band saw blade. Mc Master Carr doesn't seem to
carry it. I bought mine at Industrial Carbide Saw out of Louisville, KY.
Custom length and had it in three days. Used it tonight and all I can say is
smooth easy cutting.Very impressive. Thanks for the tip.

Was a bit pricy, but the weld is guaranteed for life and I don't see me
wearing this blade out.

Larry Diamond

  _____  

From: nsrca-discussion-bounces at lists.nsrca.org
[mailto:nsrca-discussion-bounces at lists.nsrca.org] On Behalf Of Gray E Fowler
Sent: Thursday, May 08, 2008 12:34 PM
To: General pattern discussion
Subject: Re: [NSRCA-discussion] Cutting CF and FG Panels???

Keith 

Makes sense especially to increase stifness, but I ponder the weight savings
after adding the resin and fiber especially is you are laminating with the
5.7oz 3K plain weave (most standard stuff). It is real easy to get over
strong, and landing gear usually needs a load distribution into the fuse
more than super strong gear plates.  On my firewall, built out of lite ply
by Lance, I used 2oz glass to "Strengthen" the ply..it is a waffle design so
very stiff. The idea being that the fiberglass will help keep the lite ply
from fractures-or waffle delams-disbond. Cannot get 2oz CF and the 1K CF
(4.2 oz)  that we make or canopies and chin cowls out of would be overkill. 
Have you compared weights? that would be interesting. I never have but alway
worried about it. 

How's that Guitar hero frustration game coming along for you? Any cyber
groupies yet or have you not made it to that level...like your son has...or
did you not realize your son was "involved" so to speak.

Gray Fowler
Senior Principal Chemical Engineer
Radomes and Specialty Apertures
Technical Staff Composites Engineering
Raytheon 

"Keith Black" <tkeithblack at gmail.com> 
Sent by: nsrca-discussion-bounces at lists.nsrca.org 

05/08/2008 12:17 PM 

Please respond to
General pattern discussion <nsrca-discussion at lists.nsrca.org>

To

"General pattern discussion" <nsrca-discussion at lists.nsrca.org> 

cc

Subject

Re: [NSRCA-discussion] Cutting CF and FG Panels???

I often laminate lite ply in situations where I don't think the lite ply
will be strong or stiff enough and I don't want the weight penalty of
aircraft ply. I also have laminated regular aircraft ply to give extra
strength to things like landing gear plates. This allows me to use a thinner
aircraft ply (in my mind anyways). 

Keith Black 
----- Original Message ----- 
From: Gray E Fowler <mailto:gfowler at raytheon.com>  
To: General pattern discussion <mailto:nsrca-discussion at lists.nsrca.org>  
Sent: Wednesday, May 07, 2008 4:21 PM 
Subject: Re: [NSRCA-discussion] Cutting CF and FG Panels??? 

While at work I find these blades on the machine. Somehow they magically
show up. Where you would get them??? perhaps McMaster Carr 

And what is you application that requires carbon fiber laminated on plywood?

Gray Fowler
Senior Principal Chemical Engineer
Radomes and Specialty Apertures
Technical Staff Composites Engineering
Raytheon 

"Keith Black" <tkeithblack at gmail.com> 
Sent by: nsrca-discussion-bounces at lists.nsrca.org 

05/07/2008 03:15 PM 

Please respond to
General pattern discussion <nsrca-discussion at lists.nsrca.org>

To

"General pattern discussion" <nsrca-discussion at lists.nsrca.org> 

cc

Subject

Re: [NSRCA-discussion] Cutting CF and FG Panels???

This doesn't sound like something one would find at the local hardware
store. Where can these blades be found? 

BTW, what if you have aircraft ply laminated with carbon fiber? I would
think in this case one would need a blade with teeth. 

Keith Black 
----- Original Message ----- 
From: Gray E Fowler <mailto:gfowler at raytheon.com>  
To: General <mailto:nsrca-discussion at lists.nsrca.org>  pattern discussion 
Sent: Wednesday, May 07, 2008 8:31 AM 
Subject: Re: [NSRCA-discussion] Cutting CF and FG Panels??? 

Larry 

The proper bandsaw blade for composites does not have any teeth on it at
all.  The blade consists of a coating of tungsten carbide bits like rough
sandpaper grit adhered to the leading edge of the band. The blade cuts by
abrasion and will break before it wears out. Any blade with teeth is bad for
composites as it will dull and the teeth can grab and delaminate the
sustrate or your bond to the honeycomb.

Gray Fowler
Senior Principal Chemical Engineer
Radomes and Specialty Apertures
Technical Staff Composites Engineering
Raytheon 

"Lisa & Larry" <lld613 at psci.net> 
Sent by: nsrca-discussion-bounces at lists.nsrca.org 

05/06/2008 08:59 PM 

Please respond to
General pattern discussion <nsrca-discussion at lists.nsrca.org>

To

"NSRCA" <nsrca-discussion at lists.nsrca.org> 

cc

Subject

[NSRCA-discussion] Cutting CF and FG Panels???

What is the best blade to use on a band saw? It has 2 speeds, what is the
best speed (1,450 / 3,000 rpm)?

I need to cut down two 12 x 24 panels and would like a clean edge ( 1/8"
CF/Nomex/CF panel, and a FG/Nomex/FG panel) .

Nope, don't use the band saw much..

Thanks, 

Larry Diamond_______________________________________________
NSRCA-discussion mailing list
NSRCA-discussion at lists.nsrca.org
http://lists.nsrca.org/mailman/listinfo/nsrca-discussion 

  _____  

_______________________________________________
NSRCA-discussion mailing list
NSRCA-discussion at lists.nsrca.org
http://lists.nsrca.org/mailman/listinfo/nsrca-discussion____________________
___________________________
NSRCA-discussion mailing list
NSRCA-discussion at lists.nsrca.org
http://lists.nsrca.org/mailman/listinfo/nsrca-discussion 

  _____  

_______________________________________________
NSRCA-discussion mailing list
NSRCA-discussion at lists.nsrca.org
http://lists.nsrca.org/mailman/listinfo/nsrca-discussion____________________
___________________________
NSRCA-discussion mailing list
NSRCA-discussion at lists.nsrca.org
http://lists.nsrca.org/mailman/listinfo/nsrca-discussion 

-------------- next part --------------
An HTML attachment was scrubbed...
URL: http://lists.nsrca.org/pipermail/nsrca-discussion/attachments/20080517/5f537fba/attachment-0001.html 